Divinycell H

Manufacturer

DIAB

Description

Divinycell H has been widely used over many years in virtually every application area where sandwich composites areemployed including the marine (leisure, military and commercial), land transportation, wind energy, civil engineering/infrastructure and general industrial markets.

Application


Properties

Property Method Unit H35 H45 H60 H80 H100 H130 H160 H200 H250
Compressive Strength2
ASTM D 1621
MPa
0.45
0.6
0.9
1.4
2.0
3.0
3.4
5.4
7.2
psi
65
87
130
203
290
435
493
783
1,044
Compressive Modulus2
ASTM D 1621
MPa
40
50
70
90
135
170
200
310
400
psi
5,800
7,250
10,150
13,050
19,575
24,650
29,000
44,965
58,015
Tensile Strength2
ASTM D 1623
MPa
1.0
1.4
1.8
2.5
3.5
4.8
5.4
7.1
9.2
psi
145
203
261
363
508
696
783
1,030
1,334
Tensile Modulus2
ASTM D 1623
MPa
49
55
75
95
130
175
205
250
320
psi
7,105
7,975
10,875
13,775
18,850
25,375
29,730
36,250
46,400
Shear Strength
ASTM C 273
MPa
0.4
0.56
0.76
1.15
1.6
2.2
2.6
3.5
4.5
psi
58
81
110
167
232
319
377
508
653
Shear Modulus
ASTM C 273
MPa
12
15
20
27
35
50

73

73
97
psi
1,740
2,175
2,900
3,915
5,075
7,250
10,590
10,590
14,070
Shear Strain
ASTM C 273
%
9
12
20
30
40
40
40
45
45
Nominal Density1
ISO 845
kg/m³
38
48
60
80
100
130
160
200
250
lb/ft³
2.4
3.0
3.8
5.0
6.3
8.1
10.0
12.5
15.6
1. Typical density variation ± 10%
2. Perpendicular to the plane. All values measured at +23°C (73.4°F).

Having Problems Viewing a File?

 get adobe reader MSDS documents are in Adobe PDF format. To view PDF files, you must have Adobe Acrobat installed on your computer. Download the free Adobe Acrobat reader.

Note: Technical information furnished is based on laboratory findings and is believed to be correct. No warranties of any kind are made except that the materials are of standard quality. All risk and liabilities arising from handling, storage and use of product, as well as compliance with applicable legal restrictions rest with the user. Nothing herein is to be taken as permission, inducement or recommendation to practice any patented invention or process without a license.